Oatey 53185 Rosin Core Wire Solder Oatey 53023 Rosin Leaded Core Solder Oatey 53012 Rosin Leaded Core Solder
Alloy of 60 percent Tin and 40 percent Lead; no external flux is needed. 361 degrees F ? 375 degrees F melting range. Can be used for electrical applications including wiring and other fine electronic work. Contains lead. Not for use on drinking water lines. Alloy of 60 percent Tin and 40 percent Lead; no external flux is needed. 361 degrees F ? 375 degrees F melting range. Can be used for electrical applications including wiring and other fine electronic work. Contains lead. Not for use on drinking water lines. 40 percent tin and 60 percent lead alloy with non-corrosive and non-conductive core flux for electrical and electronic soldering such as appliance repair, radio, TV, wiring motors and non-drinking water lines; melting range of 361 to 460 degrees F.
Safe-Flo 53061 Wire Solder Oatey 53010 Wire Solder Oatey 53174 Acid Core Wire Solder
Alloy of tin, silver, copper and bismuth; works with any high grade paste or liquid flux and a standard propane torch. Oatey No.95 tinning flux recommended. Provides excellent flow and fill characteristics with a melting range of 420 to 460 degrees F;  .084" diameter. Used for tin plate work, sheet metal seaming, and hot water heating lines. Meets requirements of Safe Drinking Water Act for use on copper potable water lines. 50 percent tin and 50 percent lead, used with an external flux. Good flow characteristics and low melting point. 361 to 421 degrees Fahrenheit melting range; 0.075" diameter. Used for soldering galvanized gutters, general repairs, radiators, sheet metal and non-drinking water lines. Contains lead, not to be used for plumbing applications. Lead free alloy of 95 percent Tin and 5 percent Antimony. Acid flux is contained within the core. Used for for sheet metal, radiator, gutter repair work with a melting range of 450 degrees F-464 degrees F; .081" gauge
Oatey 53011 Leaded Acid Core Solder SLDR 40/60-1/4LB 1/8IN        Oatey 53019 Instant Wire Solder
40 percent tin and 60 percent lead alloy with acid flux contained in wire core; no external flux necessary. For sheet metal work, auto radiator repair, steel gutters and more. Not for use in electrical applications. 361 to 460 degrees Fahrenheit melting range. 0.081" diameter. Contains lead, NOT for plumbing applications. 40 percent tin, 60 percent lead. For sweat fittings, sheet metal joints, gutter work and other big jobs. Works well on galvanized sheet, copper, steel, nickel plate, brass and tin plate. Tensile Strength: 4900 PSI. Melting Temp: 460? (238? C). NOT FOR ELECTRICAL CONNECTIONS. Easy to use; solder and flux all in one. Can be used on drinking water lines. Includes acid brush.
SOLDER 1/8IN SW40TIN/60L 1/4LB Oatey 53016 Rosin Core Solder SOLDER 3/32IN 40TIN/60L 1/4 LB
40 percent tin, 60 percent lead. Use with appropriate type flux such as Forney 38120, Ruby Fluid, Forney 38125, Paste Flux, or Forney 38127 & 38128, Hi-Temp Fluxes. Tensile Strength: 4900 PSI. Melting Temp: 460? (238? C). NOT SUITABLE FOR ALUMINUM. 40 percent tin and 60 percent lead alloy with non-corrosive and non-conductive core flux for electrical and electronic soldering such as appliance repair, radio, TV, wiring motors and non-drinking water lines; melting range of 361 to 460 degrees F. 40 percent tin, 60 percent lead. Ideal for electrical wiring connections because of its non-conductive residue. Will not cause corrosion or deterioration of electrical connections. Tensile Strength: 4900 PSI. Melting Temp: 460? (238? C).
SLDR 50/50 1/8IN 1/4LB        Oatey 53027 Wire Solder SOLDER 1/16IN 60TIN/40L 1/4LB
50 percent tin and 50 percent lead. Use with appropriate type flux such as Forney 38120, Ruby Fluid, Forney 38125, Paste Flux, or Forney 38127 & 38128, Hi-Temp Fluxes. Tensile Strength: 5500 PSI. Melting Temp: 421? (216? C). NOT SUITABLE FOR ALUMINUM. Lead free alloy of 95 percent Tin and 5 percent Antimony. Most commonly used where frequent and extreme temperature changes and vibrations occur. Meets the requirements of the Safe Water Drinking Act; 450 degrees F ? 464 degrees F melting range. 60 percent tin, 40 percent lead. Ideal for electrical wiring connections because of its non-conductive residue. Will not cause corrosion or deterioration of electrical connections. Tensile Strength: 6900 PSI. Melting Temp: 375? (190? C).
Oatey 53015 Acid Core Wire Solder Safe-Flo 53062 Wire Solder Oatey 53176 Acid Core Wire Solder
40 percent tin-60 percent lead, .125" gauge; can not be used on drinking lines. Alloy of tin, silver, copper and bismuth. Works with any high grade paste or liquid flux and a standard propane torch. Oatey No.95 tinning flux recommended. Provides excellent flow and fill characteristics with a melting range of 420 to 460 degrees F;  0.117" diameter. Used for tin plate work, sheet metal seaming, and hot water heating lines. Meets requirements of Safe Drinking Water Act for use on copper potable water lines. Lead free alloy of 95 percent Tin and 5 percent Antimony. Acid flux is contained within the core. Used for for sheet metal, radiator, gutter repair work with a melting range of 450 degrees F-464 degrees F; .081" gauge
SOLDER WIRE KITS WATER SOLUBLE Oatey 50193 Acid Core Wire Solder SOLDER 1/8IN 95TIN/5ANT 1/4 LB
General uses: solder pipes, brazing metal, plumbing and automotive repairs. Product details: wire melting temperature: 450 degree F; diameter: 0.062"; wire net weight: .75 oz. silver solder; .5 oz. water soluble paste flux - NSF certified to ANSI/NSF61. Kit contents: 3 oz. solid wire solder, 1 oz. water soluble paste flux, 2-1/4" acid brush, abrasive cloth. Alloy of 40 percent Tin and 60 percent Lead. For repairing galvanized gutters, filling metal seams and other general repairs with a melting range of 360 degrees F - 460 degrees F. Can not be used on drinking water lines; .081" gauge. Tin-antimony "lead-free" solder can be used for soldering potable water pipe joints. Good for plumbing, refrigeration systems and other non-electrical applications where strength is required.
Oatey 53014 Leaded Wire Solder SOLDER COMM 1/8IN 1LB RSN CRE SOLDER 1/8IN AC30TIN/70L 1/2LB
50 percent tin and 50 percent lead; use of flux required; .125" gauge. General purpose solder for sheet metal work, auto radiator repair and steel gutters. Contains lead, NOT for plumbing applications. Ideal for electrical wiring connections because of its non-conductive residue. Will not cause corrosion or deterioration of electrical connections. Melting Temp: 575? (299? C). 30 percent tin, 70 percent lead. For sweat fittings, sheet metal joints, gutter work and other big jobs. Works well on galvanized sheet, copper, steel, nickel plate, brass and tin plate. Tensile Strength: 4500 PSI. Melting Temp: 491? (255? C). NOT FOR ELECTRICAL CONNECTIONS.
Safe-Flo 50683 Wire Solder Kit SOLDER COMM ACID CRE 1LB 1/8IN Oatey 50192 Solid Wire Solder
Alloy of tin, silver, copper and bismuth. Meets requirements of Safe Drinking Water Act for use on copper potable water lines. Provides excellent flow and fill characteristics. 420 to 460 degrees Fahrenheit melting range. Includes 8 oz. solid wire solder 0.117" diameter, 1.7 ozs. No.95 lead free tinning flux, acid brush, sand cloth, and how-to instructions. For sweat fittings, sheet metal joints, gutter work and other big jobs. Works well on galvanized sheet, copper, steel, nickel plate, brass and tin plate. Melting Temp: 575? (299? C). NOT FOR ELECTRICAL CONNECTIONS. Alloy of 50 percent tin and 50 percent lead, use with Oatey #5 paste or liquid flux. Used for sheet metal, galvanized gutters, general repairs and non drinking water lines. Not to be used for plumbing. .125" gauge. Contains lead, NOT for plumbing applications.
Safe Flo H-20-5 50691 Lead Free Flux Solder Kit SOLDER 1/8IN SW 50/50 1/2LB   SOLDER 1/8IN LF S-WIRE 1/4 LB
IAPMO Listed solder and water soluble flux NSF-61. Flux meets ASTM B-813 standard and is City of L.A. approved. Lead free silver solder meets ASTM B-32 standard. Kit contains: 8 oz., .117" gauge silver lead free solder, 1.7 Oz. H-20-5 water soluble flux, an applicator brush and a sand cloth. 50 percent tin and 50 percent lead. Use with appropriate type flux such as Forney 38120, Ruby Fluid, Forney 38125, Paste Flux, or Forney 38127 & 38128, Hi-Temp Fluxes. Tensile Strength: 5500 PSI. Melting Temp: 421? (216? C). NOT SUITABLE FOR ALUMINUM. Highly recommended for potable water pipe joints, plumbing, refrigeration systems and non-electrical applications. Does not char. Flows evenly within the joint and has a low melting point. Hardens into a shiny fillet. Leaves no corrosive residue. Grade: 95/4.5/.5 Tin/Copper/Silver. Tensile Strength: 6400 PSI; Melting Temp: 430? (222? C).
Oatey 20019 Wire Solder Safe-Flo 29024 Wire Solder SOLDER 1/8IN 95TIN/5ANT 1/2 LB
Alloy of 50 percent tin and 50 percent lead, use with Oatey #5 paste or liquid flux. Used for sheet metal, galvanized gutters, general repairs and non drinking water lines. Not to be used for plumbing. .125" gauge. Contains lead, NOT for plumbing applications. Alloy of Tin, Copper, Silver, and Bismuth that works much like 50/50 solder. Recommended for use on potable water systems for sweating copper joints. Also effective on stainless steel, brass alloys, chrome alloys, galvanized steel and cast iron piping.  Works with any high grade paste or liquid flux and a standard propane torch. Oatey No.95 tinning flux recommended. Provides excellent flow and fill characteristics. 420 to 460 degrees F melting range; 0.117" diameter. Meets ASTM standard B-32 and the requirements of Safe Drinking Water Act. Can Not Be Used On Aluminum. Tin-antimony "lead-free" solder can be used for soldering potable water pipe joints. Good for plumbing, refrigeration systems and other non-electrical applications where strength is required.
Oatey 21018 Wire Solder KIT SOLDER SILVER SS TUBE     SOLDER 1/8IN LEADFREE SW 1/2LB
Alloy of 40 percent Tin and 60 percent Lead; 361 degrees F-460 degrees F melting range. Commonly used for tin plating, seaming joints, copper DWV systems and sheet metal repair. Contains lead, NOT for plumbing applications. Premium high strength acid flux cored silver bearing solder for joining all metals except aluminum, magnesium and zinc die cast. 6% silver content. Stays birght and hard. Nontoxic. Joint strength up to 20,000 PSI tensile strength. Weight: 9 oz. Working temperature: 431? F (221.7? C). Application temperature: 400? F to 700? F (204? C to 371? C). Highly recommended for potable water pipe joints, plumbing, refrigeration systems and non-electrical applications. Does not char. Flows evenly within the joint and has a low melting point. Hardens into a shiny fillet. Leaves no corrosive residue. Grade: 95/4.5/.5 Tin/Copper/Silver. Tensile Strength: 6400 PSI; Melting Temp: 430? (222? C).
Oatey 21305 Bar Solder SOLDER 1/8IN50/50 SOLIDWIRE1LB SOLDER 1/8IN COM SOLIDWIRE 1LB
Alloy of 50 percent Tin and 50 percent Lead; 361 degrees F ? 421 degrees F melting range. For use with copper drain piping, tin plating, seaming joints and sheet metal. Not for use on drinking water lines. For general purpose use with appropriate type flux such as Forney 38120, Ruby Fluid, Forney 38125, Paste Flux, or Forney 38127 & 38128, Hi-Temp Fluxes. NOT SUITABLE FOR ALUMINUM. 5500 PSI Melting Temp: 421degrees (216 degrees C). For general purpose use with appropriate type flux such as Forney 38120, Ruby Fluid, Forney 38125, Paste Flux, or Forney 38127 & 38128, Hi-Temp Fluxes. NOT SUITABLE FOR ALUMINUM. Melting Temp: 575 degrees (299 degrees C).
Oatey 53171 Rosin Core Wire Solder Oatey 21212 Rosin Leaded Core Solder Oatey 21115 Leaded Acid Core Solder
Lead free alloy of 95 percent Tin and 5 percent Antimony. 450 degree F ? 464 degree F melting range. Most commonly used where frequent and extreme temperature changes and vibrations occur. Contains lead, NOT for plumbing applications. 40 percent tin and 60 percent lead alloy with non-corrosive and non-conductive core flux for electrical and electronic soldering such as appliance repair, radio, TV, wiring motors and non-drinking water lines; melting range of 361 to 460 degrees F. 40 percent tin-60 percent lead, .125" gauge; can not be used on drinking lines.
Oatey 20015 Leaded Core Solder Safe-Flo 29025 Wire Solder SOLDER 1/8IN LEAD FREE SW 1 LB
Alloy of 50 percent tin and 50 percent lead. General purpose solder for sheet metal work, auto radiator repair and steel gutters. Not to be used on drinking water lines. .125" gauge. Contains lead, NOT for plumbing applications. Alloy of Tin, Copper, Silver, and Bismuth that works much like 50/50 solder. Recommended for use on potable water systems for sweating copper joints. Also effective on stainless steel, brass alloys, chrome alloys, galvanized steel and cast iron piping.  Works with any high grade paste or liquid flux and a standard propane torch. Oatey No.95 tinning flux recommended. Provides excellent flow and fill characteristics. 420 to 460 degrees F melting range; 0.117" diameter. Meets ASTM standard B-32 and the requirements of Safe Drinking Water Act. Can Not Be Used On Aluminum. Highly recommended for potable water pipe joints, plumbing, refrigeration systems and non-electrical applications. Does not char. Flows evenly within the joint and has a low melting point. Hardens into a shiny fillet. Leaves no corrosive residue. Grade: 95/4.5/.5 Tin/Copper/Silver. Tensile Strength: 6400 PSI; Melting Temp: 430? (222? C).
SOLDER 1/8IN 95TIN/5ANT 1 LB  Oatey 22018 Lead Free Plumbing Solder
Tin-antimony, lead free, can be used for soldering potable water pipe joints. Good for plumbing, refrigeration systems and other non-electrical applications where strength is required. Tensile Strength: 6000 PSI. Melting Temp: 464? (240? C). Lead free alloy of 95 percent Tin and 5 percent Antimony. Most commonly used where frequent and extreme temperature changes and vibrations occur. Meets the requirements of the Safe Water Drinking Act; 450 degrees F ? 464 degrees F melting range.
   
 